Sr0.95Ti0.30Fe0.70O3-d cathode cell stability test under 0.5 A cm−2 at 700 °C

This dataset contains results of cell stability tests for SOFCs with Sr0.95Ti0.3Fe0.7O3-δ  cathode sintered at 800 °C. Characterisation of the fuel cells was performed on an Open Flanges™ test setup by Fiaxell. The fuel cell were heated up to 750 °C (3 °C min-1) for reduction and then cooled down to 700 °C for the main test after 24 h stabilisation. Fuel cell tests were conducted with the total flow rates of 100 ml min-1 and 200 ml min-1 on anode and cathode side, respectively. Solartron 1260/1287 frequency analyser was used for measurement. Curent density applied for tests was 0.5 A cm-2.

本数据集包含以800℃烧结的Sr0.95Ti0.3Fe0.7O3-δ阴极固体氧化物燃料电池（Solid Oxide Fuel Cell，SOFC）的电池稳定性测试结果。采用Fiaxell公司的Open Flanges™测试装置完成该类燃料电池的表征工作。测试流程为：先以3℃·min⁻¹的升温速率将燃料电池加热至750℃进行还原，经24小时稳定后，冷却至700℃开展主体测试。燃料电池测试的阳极侧与阴极侧总流量分别为100 mL·min⁻¹与200 mL·min⁻¹。本次测试采用Solartron 1260/1287型频率分析仪完成，施加的电流密度为0.5 A·cm⁻²。