Test data for uniaxial creep on material ALLOY 800H at 800 Celsius and a stress of 34.35 MPa

The creep rupture data in this collection were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the candidate constructional alloys for service at temperatures up to 950°C. Several batches of each alloy were investigated and special attention was given to the effects of the service environments (helium containing different impurity gases, such as hydrogen, water vapour, carbon monoxide and methane, all at microbar levels, and methane reforming gas mixture) on the properties. In the test machines, these test environments led to carburisation of test pieces. However, analysis of the data showed that the stress rupture data for tests in air, in impure helium and in methane reforming gas lay in the same scatterband at each temperatures tested.

The data were used for the formulation of draft nuclear design rules for the high temperature reactor systems, which are summarised in 'Proceedings of the Workshop on Structural Design Criteria for HTR', G Breitbach, F Schubert, H Nickel, Jül-Conf-71, April 1989, Berichte der Kernforschungsanlage Jülich GmbH, ISSN 0344-5798.

本数据集收录的蠕变断裂（creep rupture）数据，源自德意志联邦共和国与北莱茵-威斯特伐利亚州的高温反应堆（high temperature reactor）项目（含直接循环氦气轮机项目、核工艺热项目及区域供热项目），旨在验证候选结构合金（candidate constructional alloys）在最高950°C温度下的服役适用性。研究人员针对每种合金分析了多批次试样，并重点关注服役环境（service environments）对材料性能的影响——所述环境包括含微量杂质气体的氦气（如氢、水蒸气、一氧化碳、甲烷，均为微巴级（microbar levels））及甲烷重整气体混合物。在测试设备中，这些环境导致试样发生渗碳（carburisation）；但数据分析显示，空气、不纯氦气及甲烷重整气体环境下的应力断裂（stress rupture）数据，在各测试温度下均处于同一分散带（scatterband）。

上述数据被用于制定高温反应堆系统的核设计规则（nuclear design rules）草案，相关成果总结于《高温反应堆结构设计准则研讨会论文集》（*Proceedings of the Workshop on Structural Design Criteria for HTR*），作者为G. Breitbach、F. Schubert与H. Nickel，会议编号Jül-Conf-71，1989年4月出版，收录于《于利希核研究中心报告》（*Berichte der Kernforschungsanlage Jülich GmbH*），ISSN号0344-5798。