Web3D visualizations of corrosion pits development for EB-PBF additively manufactured 316L SS

This collection includes online interactive Web3D visualizations of the original pores and corrosion pits in a lathe-machined (Sample 1) and as-built (Sample 2) 316L SS samples fabricated via electron beam powder bed fusion (EB-PBF) additive manufacturing. The corrosion pits were induced by immersing the sample in a 6 wt% ferric chloride solution. The sample was taken out of the solution after every 8 hours for X-ray CT and DCM analysis.

本数据集包含车床加工（样品1）和成型态（样品2）的316L不锈钢（316L SS）样品中原始孔隙与腐蚀坑的在线交互式Web3D可视化内容，这些样品通过电子束粉末床熔融（EB-PBF）增材制造制备。腐蚀坑通过将样品浸入6 wt%的三氯化铁溶液中诱导产生。每8小时将样品从溶液中取出，进行X射线计算机断层扫描（X-ray CT）和DCM分析。