Test data for uniaxial creep on material ALLOY 800H at 800 Celsius and a stress of 38.22 MPa

The creep rupture data in this collection were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the candidate constructional alloys for service at temperatures up to 950°C. Several batches of each alloy were investigated and special attention was given to the effects of the service environments (helium containing different impurity gases, such as hydrogen, water vapour, carbon monoxide and methane, all at microbar levels, and methane reforming gas mixture) on the properties. In the test machines, these test environments led to carburisation of test pieces. However, analysis of the data showed that the stress rupture data for tests in air, in impure helium and in methane reforming gas lay in the same scatterband at each temperatures tested.

The data were used for the formulation of draft nuclear design rules for the high temperature reactor systems, which are summarised in 'Proceedings of the Workshop on Structural Design Criteria for HTR', G Breitbach, F Schubert, H Nickel, Jül-Conf-71, April 1989, Berichte der Kernforschungsanlage Jülich GmbH, ISSN 0344-5798.

本数据集收录的蠕变断裂数据，源自德意志联邦共和国及北莱茵-威斯特伐利亚州的高温反应堆项目（包括直接循环氦气轮机项目、核工艺供热项目与区域供热项目），旨在评定候选结构合金在最高950℃服役温度下的适用性。研究针对每种合金的多个批次展开，并重点考察服役环境对材料性能的影响：试验气氛涵盖含氢、水蒸气、一氧化碳、甲烷等微量（微巴级）杂质气体的氦气，以及甲烷重整混合气。在试验机内，上述试验气氛会导致试样发生渗碳现象。但数据分析显示，在空气、不纯氦气及甲烷重整气氛中开展试验得到的应力断裂数据，在各测试温度下均处于同一散布带内。

本数据集用于制定高温反应堆（High Temperature Reactor, HTR）系统的核设计规范草案，相关内容总结于《高温堆结构设计准则研讨会论文集》（G Breitbach、F Schubert、H Nickel 编，Jül-Conf-71，1989年4月，于利希核研究中心有限公司报告，ISSN 0344-5798）。