Test data for uniaxial tensile on material INCONEL 617 irr at 20 Celsius

The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas ducting. Several batches and product forms (forged bar, rolled plate, pipes and tubes) of the alloy were investigated and special attention was given to the effects of the service environments (helium containing different impurity gases, such as hydrogen, water vapour, carbon monoxide and methane, all at microbar levels, and methane reforming gas mixture) on the properties. In the test machines, these test environments led to carburisation of test pieces. However, analysis of the data showed that the stress rupture data for tests in air, in impure helium and in methane reforming gas lay in the same scatter band at each temperature tested.

The creep rupture tests were carried out in single-specimen and multi-specimen test machines. In the single specimen machines the strain was continuously monitored and strain readings were taken once a day. In the multi-specimen test rigs, there were six strings, each with a different load. There were up to eight test pieces per string and strain measurements were made by interrupting the tests, cooling to room temperature, then measuring the length of each test piece using a travelling microscope. Test interruptions for strain measurements were generally every 1000 h. The tests were carried out according to the German Standard DIN 50118 (1982).

The data (secondary creep rate, time to 1% strain, time to rupture) were used for the formulation of draft nuclear design rules for the high temperature reactor systems, which are summarised in 'Proceedings of the Workshop on Structural Design Criteria for HTR', G Breitbach, F Schubert, H Nickel, Jül-Conf-71, April 1989, Berichte der Kernforschungsanlage Jülich GmbH, ISSN 0344-5798.

In addition to the creep rupture data, Alloy 617 tensile properties, low cycle fatigue and creep crack growth data are stored in MatDB.

合金617（Alloy 617）的蠕变断裂数据，源自联邦德国与北莱茵-威斯特伐利亚州的高温反应堆项目（包括直接循环氦气轮机项目、核工艺热项目及区域供热项目），旨在评定该合金在最高950℃工况下的服役资格。合金617是氦-氦中间热交换器与热气体管道建造的首选候选合金。本研究针对该合金的多个批次与多种产品形态（锻造棒材、轧制板材、管材与管件）展开，并重点考察了服役环境对其性能的影响，服役环境涵盖含微量（微巴量级）氢、水蒸气、一氧化碳、甲烷等杂质气体的氦气，以及甲烷重整混合气体。试验过程中，上述试验环境会导致试样发生渗碳现象。但数据分析显示，在各试验温度下，空气、不纯氦气与甲烷重整气体环境下的应力断裂数据均处于同一离散带内。

蠕变断裂试验采用单试样与多试样试验机开展。单试样试验机中，应变被连续监测，且每日记录一次应变数据。多试样试验台共设有6组加载串，每组施加不同载荷，每组最多搭载8个试样。应变测量需中断试验、冷却至室温后，借助移动式显微镜测量每个试样的长度。用于应变测量的试验中断间隔通常为每1000小时一次。本试验依据德国标准DIN 50118（1982版）执行。

本数据集包含的蠕变第二阶段速率、1%应变时间、断裂时间数据，被用于制定高温气冷堆（High Temperature Reactor, HTR）系统的核设计规范草案，相关内容汇总于《高温气冷堆结构设计准则研讨会论文集》（G Breitbach、F Schubert、H Nickel编，Jül-Conf-71，1989年4月，于利希核研究中心有限公司报告，ISSN 0344-5798）。

除蠕变断裂数据外，合金617的拉伸性能、低周疲劳与蠕变裂纹扩展数据均存储于MatDB数据库中。