Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 64.77 MPa

The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas ducting. Several batches and product forms (forged bar, rolled plate, pipes and tubes) of the alloy were investigated and special attention was given to the effects of the service environments (helium containing different impurity gases, such as hydrogen, water vapour, carbon monoxide and methane, all at microbar levels, and methane reforming gas mixture) on the properties. In the test machines, these test environments led to carburisation of test pieces. However, analysis of the data showed that the stress rupture data for tests in air, in impure helium and in methane reforming gas lay in the same scatter band at each temperature tested.

The creep rupture tests were carried out in single-specimen and multi-specimen test machines. In the single specimen machines the strain was continuously monitored and strain readings were taken once a day. In the multi-specimen test rigs, there were six strings, each with a different load. There were up to eight test pieces per string and strain measurements were made by interrupting the tests, cooling to room temperature, then measuring the length of each test piece using a travelling microscope. Test interruptions for strain measurements were generally every 1000 h. The tests were carried out according to the German Standard DIN 50118 (1982).

The data (secondary creep rate, time to 1% strain, time to rupture) were used for the formulation of draft nuclear design rules for the high temperature reactor systems, which are summarised in 'Proceedings of the Workshop on Structural Design Criteria for HTR', G Breitbach, F Schubert, H Nickel, Jül-Conf-71, April 1989, Berichte der Kernforschungsanlage Jülich GmbH, ISSN 0344-5798.

In addition to the creep rupture data, Alloy 617 tensile properties, low cycle fatigue and creep crack growth data are stored in MatDB.

617合金（Alloy 617）的蠕变断裂数据源自德意志联邦共和国及北莱茵-威斯特伐利亚州的高温堆项目（包括直接循环氦气轮机项目、核工艺热项目与区域供热项目），旨在验证该合金可在最高950℃的工况下服役。617合金是氦-氦中间热交换器及热气体管道建造的首选候选合金。研究覆盖了该合金的多个批次及多种产品形态（锻棒、轧制板材、管材与管件），并重点考察了服役环境对合金性能的影响：试验所用氦气含有氢气、水蒸气、一氧化碳、甲烷等不同杂质气体，杂质分压均处于微巴级别，同时还使用了甲烷重整混合气作为环境介质。在试验设备中，上述试验环境会导致试验试样发生渗碳现象。但数据分析结果表明，在各试验温度下，空气环境、不纯氦气环境以及甲烷重整气环境下的应力断裂数据均处于同一离散区间内。

蠕变断裂试验采用单试样试验机与多试样试验机开展。单试样试验机中，应变被连续监测，且每日记录一次应变数据。多试样试验台包含六组加载单元，每组单元施加不同载荷，最多可搭载8个试验试样。应变测量需通过中断试验、冷却至室温后，使用读数显微镜测量每个试样的长度来完成，试验中断周期通常为每1000小时一次。所有试验均按照德意志联邦共和国标准DIN 50118（1982版）执行。

本数据集包含的蠕变断裂数据（第二阶段蠕变速率、达到1%应变的时间、断裂时间）被用于制定高温堆（HTR）系统的核设计规范草案，相关内容总结于《高温堆（HTR）结构设计准则研讨会论文集》（G Breitbach、F Schubert、H Nickel编，Jül-Conf-71，1989年4月，于利希核研究中心有限公司报告，ISSN 0344-5798）。

除蠕变断裂数据外，617合金的拉伸性能、低周疲劳及蠕变裂纹扩展数据均存储于MatDB数据库中。