Test data for low cycle fatigue - strain control on material ALLOY 800H at 950 Celsius

The creep rupture data in this collection were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the candidate constructional alloys for service at temperatures up to 950°C. Several batches of each alloy were investigated and special attention was given to the effects of the service environments (helium containing different impurity gases, such as hydrogen, water vapour, carbon monoxide and methane, all at microbar levels, and methane reforming gas mixture) on the properties. In the test machines, these test environments led to carburisation of test pieces. However, analysis of the data showed that the stress rupture data for tests in air, in impure helium and in methane reforming gas lay in the same scatterband at each temperatures tested.

The data were used for the formulation of draft nuclear design rules for the high temperature reactor systems, which are summarised in 'Proceedings of the Workshop on Structural Design Criteria for HTR', G Breitbach, F Schubert, H Nickel, Jül-Conf-71, April 1989, Berichte der Kernforschungsanlage Jülich GmbH, ISSN 0344-5798.

本数据集收录的蠕变断裂数据，取自德意志联邦共和国与北莱茵-威斯特伐利亚州的高温反应堆（High Temperature Reactor, HTR）项目，具体包括直接循环氦气涡轮机项目、核工艺热项目及区域供热项目，其核心目标是为最高服役温度达950℃的候选结构合金完成服役资质认证。研究人员对每种合金的多个批次开展了测试，并重点关注服役环境对材料性能的影响：测试环境涵盖含微量杂质气体（如氢气、水蒸气、一氧化碳及甲烷，分压均为微巴级别）的氦气，以及甲烷重整混合气体。在测试设备中，上述环境会导致试样发生渗碳现象。但数据分析结果显示，在各测试温度下，空气、不纯氦气及甲烷重整气体环境中得到的应力断裂数据，均处于同一离散带范围内。本数据集被用于制定高温反应堆系统的核设计规范草案，相关内容总结于《高温反应堆结构设计准则研讨会论文集》（作者：G Breitbach、F Schubert、H Nickel，会议编号Jül-Conf-71，1989年4月，出版来源：于利希核研究中心有限公司报告（Berichte der Kernforschungsanlage Jülich GmbH），ISSN 0344-5798）。