Compression tests on M30SC-DT120 laminates with fibre damage

The data connected to this file is related to a series of tests performed in the facilities at TU Delft to understand the effects of fibre failure on compressive strength of CFRP laminates.
Fibre damage has been artificially introduced during layup by manually cutting the fibres. Since fibre failure always occurs in the plies closest to the specimen surfaces, the artificially damaged specimens all contain failure in the topmost plies.
The data set contains force-displacement data for a series of compression tests on laminates without fibre damage, and on laminates containing different damage configuraitons.

本文件关联的数据来自代尔夫特理工大学（TU Delft）实验室开展的一系列试验，旨在探究纤维失效对碳纤维增强复合材料（CFRP）层合板抗压强度的影响。研究人员在铺层工艺过程中通过手工切割纤维的方式人工引入纤维损伤。鉴于纤维失效通常优先发生在最靠近试样表面的铺层中，因此所有人工损伤试样的失效均出现在最表层铺层。本数据集包含两类层合板的压缩试验力-位移数据：一类为无纤维损伤的层合板，另一类为带有不同损伤构型的层合板。