Influence of sintering temperature of porous SrTi0.65Fe0.35O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C

This dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.本数据集包含了在不同烧结温度（800℃、900℃与1000℃）下制备的多孔SrTi₀.₆₅Fe₀.₃₅O₃₋δ氧电极对称电池的电化学阻抗谱（Electrochemical Impedance Spectroscopy, EIS）测试结果。测试温度为800℃，测试气氛为合成空气，气体流量为40 mL·min⁻¹。所有测试结果均已归一化至单位电极表面积，并除以双电极的总阻抗。