Data supporting: 'Modelling and optimising hybrid process of wire arc additive manufacturing and high-pressure rolling'

Figure 7 Predicted distortion of the WAAM component after removal of clamps.<br> <br> Figure 8 Longitudinal RS distributions along the vertical path in the symmetry plane for the long mechanical models after removal of clamps, as compared to experimental measurements [4]. The flat roller (a) and slotted roller (b) were used in the rolling simulations, and the long model was based on the steady-state solution mapped from the reduced-length WAAM + IL rolling model.<br> <br> Figure 10 Concurrent evolution of temperature and longitudinal stress (a), as well as the longitudinal PS (b), in the layer 6 during WAAM deposition of layers 6-8 in conjunction with IL rolling using the flat roller. The data were collected at the top of layer 6 in the inspection plane and the rolling phases are highlighted in the yellow shaded areas.<br> <br> Figure 11 Concurrent evolution of temperature and longitudinal stress (a), as well as longitudinal PS (b), in the layer 6 during WAAM deposition of layers 9-11 in conjunction with IL rolling using the flat roller. The data were collected at the top of layer 6 in the inspection plane and the rolling phases are highlighted in the yellow shaded areas.<br> <br> Figure 12 Concurrent evolution of temperature and longitudinal stress (a), as well as longitudinal PS (b), in the layer 6 during WAAM deposition of layers 12-14 in conjunction with IL rolling using the flat roller. The data were collected at the top of layer 6 in the inspection plane and the rolling phases are highlighted in the yellow shaded areas.<br> <br> Figure 13 Concurrent evolution of the longitudinal PS and stress in the layer 9 during WAAM deposition of layers 9-16 in conjunction with IL rolling using the slotted roller. The data were collected at the top of layer 9 in the inspection plane (the slotted roller started rolling on layer 6) and the rolling phases are highlighted in the yellow shaded areas.<br> <br> Figure 18 Evolution of longitudinal PS in the layer 6 during WAAM deposition and stacked 4L rolling with flat roller. The rolling phases are highlighted in the yellow shaded areas.<br>