Mechanical performance of original; yellowish and blueish ProFile instruments: isolating heat-treatment as a variable

Abstract The present study aimed to perform two different heat-treatments in an austenitic NiTi ProFile instrument and to compare the mechanical performance of original and heat-treated instruments. Heat treatment of ProFile (tip size 25 and 0.06 taper) instruments were carried out in a furnace in argon atmosphere using a heating rate of 10° C/min. After reaching the programmed temperatures of 450 ºC or 500 ºC the system remained at a constant temperature for 10 minutes; followed by cooling in water at room temperature. Afterwards; the three groups (n=30 per group) of instruments were compared regarding their cyclic fatigue (n=10 per group); bending (n=10 per group); and buckling resistance (n=10 per group). After cyclic fatigue tests; a scanning electron microscope was used to analyze the fracture surfaces and observe the fracture mode. Statistical analysis was performed using One-way ANOVA and Student-Newman-Keuls test; with an alpha type error set at 0.05. Yellowish and blueish coloration was observed in the ProFile instruments after 450 ºC or 500 ºC heat treatments; respectively. Conventional ProFile instruments showed the lower cyclic fatigue; and the higher bending and buckling resistance (P0.05). It can be concluded that the different heat treatments performed on ProFile instruments increased its cyclic fatigue resistance and improved the flexibility and buckling resistance.