Hot isostatic pressing synergistically enhances the strength and plasticity of EV31A magnesium alloy fabricated by wire arc additive manufacturing

All the above experimental data are unprocessed raw data. Original Image for Fig.3.zip:The size distribution characteristics of pores observed by industrial CT Original Image for Fig.4.zip:The size distribution characteristics of pores observed by industrial CT Original Image for Fig.5.zip:Optical microstructure Original Image for Fig.6.zip:SEM-EDS image Original Image for Fig.7.zip:XRD Original Image for Fig.8.zip:IPF and {0001}PF maps of EBSD Original Image for Fig.10.zip:Fracture surface analysis Original Image for Fig.11.zip:DRX, KAM, Misorientation distribution maps of EBSD Original Image for Fig.12.zip:DRX, KAM, Misorientation distribution maps of EBSD Original Image for Fig.13.zip:Phase distribution map of EBSD Original Image for Fig.14.zip:The precipitation in TEM Original Image for Fig.15.zip:The precipitation in TEM Original Image for Fig.16.zip:The precipitation in TEM Original Image for Fig.17.zip:Twinning distribution map of EBSD