Internal and Marginal Fit and Fracture Strength of Narrow Diameter Dental Implant-Abutment Assembly

Abstract The aim of this study was to assess the internal and vertical marginal fit of metallic copings to abutments and the fracture strength of different narrow diameter dental implant/abutments, either submitted to thermomechanical cycling or not. Sixty-four implant/abutments (n=16) were divided into 4 groups according to diameter and abutment type: G3.5-UAC (morse taper implant Ø3.5mm + universal abutment with beveled chamfer finish); G2.9-UAS (morse taper implant Ø2.9mm + universal abutment with shoulder finish); G2.8-AA (morse taper friction implant Ø2.8mm + anatomical abutment) and G2.5-HP (one-piece implant Ø2.5mm with indexed hexagonal platform). Each group was divided into two subgroups (n=8): submitted and not submitted to thermomechanical cycling (TMC). To assess internal and vertical marginal fit of metallic copings, the assemblies were scanned using microtomography (micro-CT) (n=5). The samples were subjected to the compressive strength test on a universal test machine. Group G3.5-UAC showed the highest marginal misfit regardless of TMC (p