The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen
收藏DataCite Commons2023-03-08 更新2025-04-16 收录
下载链接：
https://mostwiedzy.pl/en/open-research-data/the-xrd-diffraction-patterns-of-la0-3sr0-6ce0-1-0-9me0-1ti0-9o3-d-me-co-cu-fe-mn-ni-materials-after-reduction-at-1000-deg-c-in-hydrogen,30708120636986-0
下载链接
链接失效反馈官方服务：
资源简介：
The (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground in an agate mortar, pressed back into pellets, heated in an oven at 1400 °C for 12 hours and cooled to room temperature at a rate of 5 °C/min. The XRD analysis allowed for determining the phase composition of powders after reduction at 1000 deg.C in hydrogen.
提供机构：
Gdańsk University of Technology
创建时间：
2023-03-07