Effect of the Bis-Dimethylamino Benzydrol Coinitiator on the Mechanical and Biological Properties of a Composite

Abstract To examine the effect of the alternative coinitiator 4,4’bis dimethylamino benzydrol (BZN) in degree of conversion (DC), mechanical and biological properties of experimental composites. The coinitiator BZN was used in three concentrations (0.2, 0.5 and 1.2%), and the coinitiator DMAEMA was used as control at the same concentrations as above. The molar concentration of camphorquinone (CQ) and coinitiators was kept constant (1:1). The composites were manipulated and submitted to microhardness test (VHN), flexural and compressive strength (in MPa), elastic modulus (GPa), DC (FT-IR) and in vitro cytotoxicity (against 3T3 fibroblastic cells) of the experimental resins. Data were subjected to two-way ANOVA and Tukey post-test (α=0.05). The experimental composite resin with BZN showed higher DC values compared to control DMAEMA groups. For the mechanical properties, microhardness values were higher in BZN groups; flexural strength and elastic modulus were similar between all the groups. Compressive strength for groups BZN0.5 and DMAEMA0.5 were not statistically different, being the lowest values attributed to group BZN0.2. The experimental resins with BZN and DMAEMA were considered nontoxic against 3T3 fibroblasts. The inclusion of the coinitiator BZN in experimental composites was considered nontoxic against 3T3 fibroblast cells, without compromising DC and mechanical properties.