Correlation between Bond Strength to Dentin and Sealers Penetration by Push-Out Test and CLSM Analysis

收藏
DataCite Commons2020-08-26 更新2024-08-17 收录
下载链接:
https://scielo.figshare.com/articles/Correlation_between_Bond_Strength_to_Dentin_and_Sealers_Penetration_by_Push-Out_Test_and_CLSM_Analysis/11314682
下载链接
链接失效反馈
官方服务:
资源简介:
Abstract This study correlated the bond strength (BS) and dentin penetration of different sealers by push-out test and Confocal Laser Scanning Microscopy (CLSM) analysis. Forty-five root canals were prepared according to the crown-down technique and filled with gutta-percha associated to the following sealers (n=15): Endofill, AH Plus and MTA Fillapex. Five canals of each group were filled with the sealers added with 0.1% Rhodamine B dye. Next, the specimens were transversely sectioned and submitted to the push-out test (n=10) and CLSM analysis (n=5). The BS data showed the following means (MPa) and standard deviation: AH Plus (4.17±1.86); MTA Fillapex (3.13±1.96) and Endofill (2.10±1.03). Statistical analysis (two-way ANOVA, α=0.05) showed significant difference among sealers (p<0.001) and root canal thirds (p<0.001). The BS results of Endofill and MTA Fillapex were statistically similar (p>0.05), however, they were statistically different from AH Plus (p<0.001). The regional analysis of BS showed similarity between middle and apical thirds (p>0.05), and both were different from coronal portion (p<0.001). CLSM analysis verified tags formation in all groups and higher penetration of the specimens filled with AH Plus (p<0.05). The Kendall test (correlation between BS to dentin and sealer penetration into dentinal tubules) and the Pearson test (between failures pattern and sealer penetration into dentinal tubules) did not show correlation between the variables evaluated for all the tested sealers (p>0.05). AH Plus group had higher BS to dentin, and deeper tags formation than the other sealers. There was no significant correlation between BS and intratubular penetration of the tested sealers.
提供机构:
SciELO journals
创建时间:
2019-12-04
二维码
社区交流群
二维码
科研交流群
商业服务