Efect of Nanoscale Cu‑Riched Clusters on Strength and Impact Toughness in a Tempered Cu‑Bearing HSLA Steel

The efect of Cu-riched clusters on strength and impact toughness in a tempered Cu-bearing high-strength low-alloy (HSLA) steel is investigated. With increasing the tempering temperature, it is found that the yield strength increases frstly, achieving the maximum value (~ 1053 MPa) at the tempering temperature of 450 °C, and then decreases signifcantly with the rise of tempering temperature. The tempering temperature-dependent yield strength is closely related to the precipitation of Cu-riched clusters. When tempering at 450 °C, the peak strength will be reached as the nanoscale Cu-riched clusters with small size and high number density will cause a strong precipitation strengthening (~492 MPa) due to the dislocation shearing mechanism. However, the Cu-riched clusters will coarsen with further increasing tempering temperature, resulting in obvious decrement of yield strength owing to the dislocation bypassing mechanism. Compared with the yield strength, the variation in impact energy displays an inverse tendency and the impact energy is only 7 J for the sample tempered at 450 °C. The fracture mode can be well explained by the competition between the cleavage fracture strength (σF) and “yield strength” (σY). Although transgranular cleavage fracture can be found in samples tempered at 450 and 550 °C, the crack propagation along the lath boundaries is prevented in the sample tempered at 550 °C. The reason is that the number density of Cu-riched clusters at lath boundaries decreases and the segregation of Mo element at the lath boundaries is induced, which will increase the bonding energy.