Optimization of magnetic properties in fast consolidated SrFe12O19 nanocrystallites

The work contains 5 figures and the datasets corresponding to each figure are included in separate folders in form of .xy format or .png format. 1) The folder “Fig1” contains the “Fig1.png” which illustrates the SPS sintering conditions regarding the heating rate, dwelling time and the applied uniaxial pressure. The lower part of the figure is an illustration of the setup used at the pre/alignment of particles in an external magnetic field up to 0.55 Tesla. 2) The folder “Fig2” contains the powder X-ray data measured for different Sr/Fe molar ratios (“SrFe1I2_data.xy”, “SrFe1I4_data.xy”, “SrFe1I6_data.xy”,” SrFe1I8_data.xy) and the calculated data based on Rietveld refinement by using FullProf (“SrFe1I2_calculated.xy”, “SrFe1I4_ calculated xy”, “SrFe1I6_ calculated.xy”,” SrFe1I8_ calculated.xy”). The .xy files contain two tab delimited columns. The first column represent the 2theta diffraction angle and the second column gives the arbitrary intensities. “Figure2.png” gives the weight percentages of the different chemical phases detected in the powders while the lower part of the figure gives the crystallites sizes calculated by FullProf program. 3) The folder “Fig3” contains the magnetization data in a form of hysteresis loops measured at room temperature. Each file contains 3 columns. First column represent the applied external magnetic field (Oe units), the second column is the emu while the third column represents the emu/grams units. 4) The folder “Fig4” contains the oriented volume fraction data. Each file is a 2 columns data. The tilting angle k is given in the first column while the oriented volume fraction is given in the second column. “Fig4.png” show the pole figures obtained from x-ray diffraction measurements. 5) The folder “Fig5” gives the data repository for hysteresis loops measured at room temperature. Here the effect of external magnetic field influence prior compaction was studied. Four data sets are included here. “H_0.15T “, “H_0.45T”, “H_0.55T” and “H_0.15T_t2min. The columns are the same as described for folder “Fig3”.