Spectroscopic ellipsometry mapping of PAAO:Au (AJ-2-04-20-Au sample)

Spectroscopic ellipsometry measurement data obtained from the porous anodized aluminum oxide covered with gold nanoparticles (PAAO:Au). The sample was made by anodization of aluminum monocrystal in 0.3 mol/L oxalic acid at 40 V for 3 minutes and 37 seconds. Then it was dip-coated in 60 nm diameter gold nanoparticles suspension. Extraction speed was 500 nm/s. The measurements were carried out at 20 × 20 locations covering all of the sample surface (approximately 4.8 × 4.8 mm2). The coordinates of each of 400 locations are available in "mapping_points.csv" file. All measurement data is also included in a single "AJ-2-04-20-Au Ellipsometry Mapping Measurements.rar" file. Ellipsometer: rotating compensator GES5-E (Semilab). Light source: 75 W xenon short arc lamp with 185-2000 nm wavelength spectrum. Detector: UV-Vis CCD with 0.8 nm resolution. Spectral range: approximately 230-960 nm. Light incidence angles: 50°, 55°, 60°, 65°, 70°, 75°. Light beam size: microspot (365 × 470 μm2 at 75° angle of incidence). The same sample was also measured using the same spectroscopic ellipsometry method before being covered with gold nanoparticles. The data can be found here: https://doi.org/10.5281/zenodo.5718202