Mixed Valence Europium Nitridosilicate Eu₂SiN₃

The mixed valence europium nitridosilicate Eu2SiN3 has been synthesized at 900 °C in welded tantalum ampules starting from europium and silicon diimide Si(NH)2 in a lithium flux. The structure of the black material has been determined by single-crystal X-ray diffraction analysis (Cmca (no. 64), a = 542.3(11) pm, b = 1061.0(2) pm, c = 1162.9(2) pm, Z = 8, 767 independent reflections, 37 parameters, R1 = 0.017, wR2 = 0.032). Eu2SiN3 is a chain-type silicate comprising one-dimensional infinite nonbranched zweier chains of corner-sharing SiN4 tetrahedra running parallel [100] with a maximum stretching factor fs = 1.0. The compound is isostructural with Ca2PN3 and Rb2TiO3, and it represents the first example of a nonbranched chain silicate in the class of nitridosilicates. There are two crystallographically distinct europium sites (at two different Wyckoff positions 8f) being occupied with Eu2+ and Eu3+, respectively. 151Eu Mössbauer spectroscopy of Eu2SiN3 differentiates unequivocally these two europium atoms and confirms their equiatomic multiplicity, showing static mixed valence with a constant ratio of the Eu2+ and Eu3+ signals over the whole temperature range. The Eu2+ site shows magnetic hyperfine field splitting at 4.2 K. Magnetic susceptibility measurements exhibit Curie−Weiss behavior above 24 K with an effective magnetic moment of 7.5 μB/f.u. and a small contribution of Eu3+, in accordance with Eu2+ and Eu3+ in equiatomic ratio. Ferromagnetic ordering at unusually high temperature is detected at TC = 24 K. DFT calculations of Eu2SiN3 reveal a band gap of ∼0.2 eV, which is in agreement with the black color of the compound. Both DFT calculations and lattice energetic calculations (MAPLE) corroborate the assignment of two crystallographically independent Eu sites to Eu2+ and Eu3+.