Improved electro-optical and dielectric properties of polymer dispersed liquid crystal doped with disperse dye red 1 and carbon nanoparticles

Disperse dye red 1 (DR1) and carbon nanoparticles (CNPs) were doped separately to form polymer dispersed liquid crystal films, namely, DPDLC & CPDLC. Nematic liquid crystal (LC) and photopolymer NOA-65 were used to prepare these composite films using polymerisation-induced phase separation (PIPS) technique. In this research work, it is demonstrated that the minute concentration (0.05% wt./wt.) of DR1 and CNPs controls the LC droplet alignment and LC droplet size in polymer dispersed liquid crystal (PDLC) film. The effect of DR1 and CNPs on PDLC film has been investigated in terms of LC droplet size, transition temperature, voltage-transmittance characteristic, contrast ratio, response time, haze, and dielectric measurements. The obtained results reveal that the threshold voltage values of the composite film get reduced from 34.87 V (undoped) to 10.19 and 9.26 V, for 0.05% of DR1 and CNPs doping, respectively. The DR1 (0.05%) doped film shows improved contrast of the undoped film as compared to CNPs (0.05%) film, whereas CNPs (0.05%) doped film shows a faster response time of 2.81 ms as compared to DR1 (0.05%) doped film (3.14 ms). Dielectric analysis of undoped, DPDLC, and CPDLC films represents Debye type relaxation mode.