This dataset supports the publication "Solution-processed low resistivity zinc oxide nanoparticle film with enhanced stability using EVOH", ACS Applied Electronic Material.
The dataset includes test results for Figure 4 that can be viewed in excel format.
The figures are as follows:
Figure 4. a) The resistance of interdigitated device without any passivation obtained after different UV-vacuum-heating times. The samples were exposed to the 365 nm wavelength UV and heated to 190 °C in 10-2 mbar vacuum condition.
Figure 5. Measured time dependent sheet resistance changes. The sheet resistance is calculated from the measured resistance of the device to its W/L ratio (See Figure S2e). The lines joining the dots are only for eye guide.
Figure 7. Measured O 1s XPS spectra of ZnO NP film, a) with EVOH passivation and UV-vacuum-heat process b) without the passivation and the UV-vacuum-heat process.