Dataset for: The Effect of Loading Direction on Slip and Twinning in an Irradiated Zirconium Alloy

<strong>This is the dataset used in the following publication: </strong> R. Thomas, D. Lunt, M. D. Atkinson, J. Quinta da Fonseca, M. Preuss, F. Barton, J. O'Hanlon, and P. Frankel, "The Effect of Loading Direction on Slip and Twinning in an Irradiated Zirconium Alloy," in <em>Zirconium in the Nuclear Industry: 19th International Symposium</em>, ed. A. Motta and S. Yagnik (West Conshohocken, PA: ASTM International, 2021), 233-261. https://doi.org/10.1520/STP162220190027. <strong>Contained in this dataset are:</strong> A Jupyter notebook which uses the open-source DefDAP Python package (https://github.com/MechMicroMan/DefDAP) to open enclosed HRDIC, EBSD and image data for non-irradiated and 0.1 dpa proton irradiated Zircaloy-4 deformed to ~3% strain, along the rolling direction and transverse direction. Please use the 'develop' version of DefDAP: https://github.com/MechMicroMan/DefDAP/tree/f6b5d6ec33db9a45089fada17026432645044d2f <strong>Publication abstract:</strong> In this study, deformation experiments together with high-resolution digital image correlation were used to quantify the effect of proton irradiation on strain localization in Zircaloy-4 loaded along the rolling and transverse directions. Significant increases in strain heterogeneity were measured in the irradiated material compared to the nonirradiated material. This was a result of confinement of slip to channels in the irradiated material, which contain high effective shear strain values, with almost no strain in the regions between channels. The active slip systems in the material were also determined by comparing experimental slip trace angles from high-resolution digital image correlation with theoretical slip trace angles determined using grain orientation from electron backscatter diffraction. An increased amount of pyramidal and wavy basal slip, as well as tension twinning, were observed in the sample loaded along the transverse direction, compared to the sample loaded along the rolling direction, due to crystallographic texture. No significant change in slip system activity was observed as a result of 0.1 dpa proton irradiation, despite the dramatic change in slip pattern. The findings provide further insight into the role of irradiation on deformation behavior and provide quantitative data on slip system activation, for as-received and irradiated Zircaloy-4, against which to validate models.