Fatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)

Fatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C) Dataset presents data of fatigue life determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100 mm, h=62,1 - 63,7 mm. Additionally set presents the figures of destruction interfaces. Data was obtained in the HYD-25 hydraulic universal machine (Cooper Ltd) for 1 temperature (+20°C). Indirect tensile fatigue test was used; IT-CY scheme acc. to EN 12697-26 standard) Test load was selected as impulse loading with varied initial strain range – from 49 µm up to 205 µm.