Cs1–xRbxPbCl3 and Cs1–xRbxPbBr3 Solid Solutions: Understanding Octahedral Tilting in Lead Halide Perovskites

The structures of the lead halide perovskites CsPbCl3 and CsPbBr3 have been determined from X-ray powder diffraction data to be orthorhombic with Pnma space group symmetry. Their structures are distorted from the cubic structure of their hybrid analogs, CH3NH3PbX3 (X = Cl, Br), by tilts of the octahedra (Glazer tilt system a–b+a–). Substitution of the smaller Rb+ for Cs+ increases the octahedral tilting distortion and eventually destabilizes the perovskite structure altogether. To understand this behavior, bond valence parameters appropriate for use in chloride and bromide perovskites have been determined for Cs+, Rb+, and Pb2+. As the tolerance factor decreases, the band gap increases, by 0.15 eV in Cs1–xRbxPbCl3 and 0.20 eV in Cs1–xRbxPbBr3, upon going from x = 0 to x = 0.6. The band gap shows a linear dependence on tolerance factor, particularly for the Cs1–xRbxPbBr3 system. Comparison with the cubic perovskites CH3NH3PbCl3 and CH3NH3PbBr3 shows that the band gaps of the methylammonium perovskites are anomalously large for APbX3 perovskites with a cubic structure. This comparison suggests that the local symmetry of CH3NH3PbCl3 and CH3NH3PbBr3 deviate significantly from the cubic symmetry of the average structure.