Data underlying the research on: Al 2024-T3 center crack tension constant amplitude fatigue tests with potential drop through the cycle measurements

Al 2024-T3 center crack tension constant amplitude fatigue tests, data from potential drop measurements. The objective was to obtain the potential behavior throughout fatigue cycles, in order to observe relationships between fatigue crack growth effects such as crack tip plasticity and crack extension.