Effect of solution annealing and Al addition on the corrosion behavior of austenitic stainless steel in supercritical carbon dioxide at high temperature
收藏中国科学院兰州化学物理研究所科学数据中心2025-11-20 更新2026-01-10 收录
下载链接：
https://ggjsfwdata.licp.cn/dataDetails/2f3d432326d44f9c9e60b87f07c8d25c
下载链接
链接失效反馈官方服务：
资源简介：
The corrosion behavior of three austenitic stainless steels with basial composition of 20Cr25Ni (R1, SR1 and R1Al) was investigated in supercritical CO2 at 650℃. R1 was cold-rolled, SR1 was solution-annealed and R1Al was R1 with aluminum addition. The results indicate that solution annealing enhanced the corrosion resistance, reducing weight gain by 37.9% and mitigating preferential corrosion. Adding aluminum to R1 further improved its corrosion resistance, decreasing weight gain by 75.5% and eliminating preferential corrosion. The oxide film structure of R1 is SiO2, Mn2O3, Cr2O3 from the inside out, while that of R1Al is Al2O3, Cr2O3, and spinel oxides.