Raw data for all study groups.

Background and aim
Achieving the aesthetic standards in tooth-colored restorative materials requires close attention to their color, translucency, and resistance to discoloration. This study aimed to evaluate the effect of sintering temperature on color stability and translucency in zirconia systems with low, high, and ultra-high translucencies.
Methods
This experimental study was conducted on 60 zirconia disks with low, high and ultra-high translucencies (n = 20 per group), each group divided into subgroups to be sintered at either 1450°C or 1550°C (n = 10 per subgroup). Baseline color and translucency parameters were measured, the specimens were then immersed in coffee solution for 30 days, and the measurements were repeated post-immersion. Changes in color (ΔE) and translucency (ΔTP) were calculated via CIELAB formula and compared by using two-way ANOVA and Tukey’s post hoc test (α = 0.05).
Results
Results of two-way ANOVA showed that the ΔE was significantly different among the three zirconia translucencies (P<0.001), but no significant difference was found between the two sintering temperatures (P = 0.712). Additionally, the interaction between zirconia type and sintering temperature was not statistically significant for ΔE (P = 0.264). The low-translucency group showed significantly greater ΔE than the high-translucency and ultra-high-translucency groups (P<0.05), while the high- and ultra-high-translucency groups were not significantly different in this regard (P>0.05). Regarding the ΔTP, two-way ANOVA showed that the difference was not statistically significant either among the three zirconia types (P = 0.4430) or between the two sintering temperatures (P = 0.4544). Nor was the interaction between zirconia type and sintering temperature statistically significant (P = 0.5505).
Conclusion
It was concluded that sintering temperature had no effect on color and translucency changes after immersion in coffee. Whereas zirconia type significantly affected the color changes after immersion in coffee; with the higher-translucency zirconia types being significantly more color-stable than the low-translucency zirconia.