Reaching V2(PO4)3 by sodium extraction from single-phase NaxV2(PO4)3 (1 x 3) positive electrode materials

Dataset production context : In the present work, we report on single-phase NaxV2(PO4)3 compositions (1.5 ≤ x ≤ 2.5) of the Na super ionic conductor type, obtained from a straightforward synthesis route. Typically, chemically prepared c-Na2V2(PO4)3, obtained by annealing an equimolar mixture of Na3V2(PO4)3 and NaV2(PO4)3, exhibits a specific sodium-ion distribution (occupancy of the Na(1) site of only 0.66(4)), whereas that of the electrochemically obtained e-Na2V2(PO4)3 (from Na3V2(PO4)3) is close to 1. Unlike conventional Na3V2(PO4)3, when used as positive electrode materials in Na-ion batteries, the NaxV2(PO4)3 compositions lead to unusual single-phase Na+ extraction/insertion mechanisms with continuous voltage changes upon Na+ extraction/insertion. We demonstrate that the average equilibrium operating voltage observed upon Na+ deintercalation from single-phase Na2V2(PO4)3 is increased up to an average value of ~3.70 V versus Na+/Na (thanks to the activation of the V4+/V5+ redox couple) compared to 3.37 V versus Na+/Na in conventional Na3V2(PO4)3, thus leading to an increase in the theoretical energy density from 396.3 Wh kg–1 to 458.1 Wh kg–1. Electrochemical and chemical Na+ deintercalation from c-Na2V2(PO4)3 enables complete Na-ion extraction, increasing energy density. All these data are taken from the work of M. Sunkyu Park, Kriti Choudhary and were used to produce the article (cited below) in its initial version.