Comprehensive Study of Oxygen Storage in YbFe₂O_4+<i>x</i> (<i>x</i> ≤ 0.5): Unprecedented Coexistence of FeO_<i>n</i> Polyhedra in One Single Phase

The multiferroic LuFe2.5+2O4 was recently proposed as a promising material for oxygen storage due to its easy reversible oxidation into LuFe3+2O4.5. We have investigated the similar scenario in YbFe2O4+x, leading to a slightly greater oxygen storage (OSC) capacity of 1434 μmol O/g. For the first time, the structural model of LnFe2O4.5 was fully understood by high-resolution microscopy images, and synchrotron and neutron diffraction experiments, as well as maximum entropy method. The oxygen uptake promotes a reconstructive shearing of the [YbO2] sub-units controlled by the adaptive Ln/Fe oxygen coordination and the Fe2/3+ redox. After oxidation, the rearrangement of the Fe coordination polyhedra is unique such that all available FeOn units (n = 6, 5, 4 in octahedra, square pyramids, trigonal bipyramids, tetrahedra) were identified in modulated rows growing in plane. This complex pseudo-ordering gives rise to short-range antiferromagnetic correlation within an insulating state.