Anti-erosion effect of an experimental varnish on eroded dentin

Abstract This in vitro study evaluated the effect of an experimental varnish containing 20% nano-hydroxyapatite (nHAP) associated with 5% stannous chloride (SnCl2) against erosive-abrasive wear on bovine dentin. Samples of bovine cervical dentin were pre-eroded (0.3% citric acid, pH 2.6 for 10 minutes) and randomized into 4 groups (n=10): Control group - experimental varnish without active ingredient (CG); experimental varnish containing 20% nHAP (nHG); experimental varnish containing 5% SnCl2 (24.800 ppm Sn2+) (SnG); experimental varnish containing 20% nHAP associated with 5% SnCl2 (18.300 ppm Sn2+) (nHSnG). After applying the materials, the erosive-abrasive challenges were performed for five days. Erosive dentin loss and analysis of the pattern of dentinal obliteration were performed by 3D confocal laser microscopy. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The SnG and nHSnG experimental groups presented more effectiveness in preventing erosive wear when compared to the other groups (p