Experimental Dataset for: Synthesis and Characterization of Geopolymer Binders from Khojakul Kaolin and Takhiatash TPP Fly Ash: Effect of Curing Conditions on Microstructure and Mechanical Properties

DATASET DOCUMENTATION (README) TITLE:Experimental Dataset for: Synthesis and Characterization of Geopolymer Binders from Khojakul Kaolin and Takhiatash TPP Fly Ash: Effect of Curing Conditions on Microstructure and Mechanical Properties AUTHORS & ORCID IDs:- Yusufboy Khasanovich Yakubov (Corresponding author) ORCID: https://orcid.org/0000-0003-3852-3141 Email: [e-mail]- Sherzad Matchanov ORCID: https://orcid.org/0000-0003-0539-3045- Aida Ruzmetova ORCID: https://orcid.org/0009-0004-1008-4057- Jumaniyoz Jumaniyozov ORCID: https://orcid.org/0009-0007-9987-1381 CONTENTS OF THIS DATASET:1. Table_1_Raw_Kaolin_XRF.xlsx - Chemical composition of raw Khojakul kaolin samples (5 samples + average).2. Table_2_Metakaolin_XRF.xlsx - Chemical composition of metakaolin after thermal activation at 850 °C (5 samples + average).3. Table_3_Fly_Ash_XRF.xlsx - Chemical composition of Takhiatash TPP fly ash samples (4 samples + average).4. Table_4_EDS_Elemental_Composition.xlsx - EDS quantitative elemental distribution of geopolymer paste (Open vs Closed curing).5. Table_5_Compressive_Strength.xlsx - Compressive strength test results at 7, 14, 21, and 28 days.6. Table_6_Bulk_Density.xlsx - Bulk density measurements across all curing ages. 7. Figures/ - A folder containing all 17 high-resolution experimental and analytical figures (.tif format, from Figure 1 to Figure 17) supporting the study, including SEM images, XRD diffractograms, FTIR spectra, TGA-DSC curves, and mechanical test plots. LICENSE:Creative Commons Attribution 4.0 International (CC-BY 4.0)