Self-Supported Branched Poly(ethylenimine) Monoliths from Inverse Template 3D Printing for Direct Air Capture

3D-printed inverse templates are combined with ice templating to develop self-supported branched poly­(ethylenimine) monoliths with regular channels of varying channel density and ordered macropores. A maximum uptake of 0.96 mmol of CO2/g of monolith from ambient air containing 45.5% RH is achieved from dynamic breakthrough experiments, which is a 31% increase compared to the CO2 uptake from adsorption under dry conditions for the same duration. The breakthrough experiments show characteristics of internal mass-transfer limitations. The cyclic dynamic breakthrough experiments indicate stable operation without significant loss in CO2 uptake across eight cycles. Moreover, the self-supported monolith shows minimal loss in adsorption capacity (7.7%) upon exposure to air containing 21% oxygen at 110 °C, in comparison to a conventional sorbent consisting of poly­(ethylenimine) impregnated on Al2O3 (18.9%). The monoliths exhibit good mechanical stability, contributed by elastic deformation, corresponding to up to 74% strain and lower pressure drop compared to many existing monoliths in the literature.