Mode I fracture and fatigue behavior of thick adhesive joints with and without crack-arresting features

This dataset contains the results of mode-I fracture and fatigue experiments conducted on thick glass fiber-reinforced polymer composite-epoxy adhesive joints commonly used in wind turbine rotor blades. These joints comprise additively manufactured design elements specifically engineered to arrest cracks under quasi-static fracture and fatigue loading conditions. The dataset also includes the quasi-static tensile experimental data of composite materials and the crack-arresting features.本数据集包含针对风力涡轮机转子叶片中常用的厚型玻璃纤维增强聚合物复合材料-环氧树脂粘接接头开展的I型断裂（mode-I fracture）与疲劳实验结果。此类接头集成了专为在准静态断裂（quasi-static fracture）及疲劳载荷（fatigue loading）条件下抑制裂纹扩展而设计的增材制造（additive manufacturing）结构单元。本数据集还涵盖了复合材料的准静态拉伸实验数据以及阻裂特性相关内容。