Influence of sintering temperature of porous SrTi0.50Fe0.50O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C

This dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.本数据集收录了在800℃、900℃与1000℃三种不同烧结温度下制备的多孔SrTi0.50Fe0.50O3−δ氧电极组装的对称电池的电化学阻抗谱（Electrochemical Impedance Spectroscopy, EIS）测试结果。测试温度设定为800℃，测试气氛为合成空气，气体流量为40 mL·min⁻¹。所有测试结果均已归一化至电极表面积，并经双电极体系校正。