Raw and processed data phase relationships in the SiO2-SrO-Al2O3 system

The liquidus lines in the silica rich area of the ternary SiO2-SrO-Al2O3 phase diagram were determined experimentally at 1723 K (1450°C), 1823 K (1550°C), and 1873K (1600°C) using the quenching technique. Quenched samples were analyzed using LOM, SEM and XRD. Based on the obtained results, the liquidus lines were constructed at these three temperatures. In this table the sample compositions studied, the equilibrating temperature and the phases present are listed.本研究采用淬火法，在1723 K（1450℃）、1823 K（1550℃）与1873 K（1600℃）三个温度下，实验测定了三元SiO₂-SrO-Al₂O₃相图富二氧化硅区域的液相线。对淬火后的试样分别采用光学显微分析（Light Optical Microscopy, LOM）、扫描电子显微镜（Scanning Electron Microscopy, SEM）及X射线衍射（X-ray Diffraction, XRD）进行表征。基于所得实验结果，构建了上述三个温度下的液相线。本表格列出了本次研究所涉及的试样成分、平衡温度及检测到的物相。