Oxidation and hot corrosion behaviors of NiAlTa protective material for turbine single crystal blade tips
收藏中国科学院兰州化学物理研究所科学数据中心2025-12-09 更新2026-01-10 收录
下载链接：
https://ggjsfwdata.licp.cn/dataDetails/d171dae3a34e475495e684547b2d80c2
下载链接
链接失效反馈官方服务：
资源简介：
NiAlTa alloys were prepared to improve oxidation and hot corrosion resistance of single crystal blade tips as well as the sealing performance of an engine. The oxidation and hot corrosion behaviors of NiAlTa alloys were investigated. The results showed that NiAlTa alloys exhibited low oxidative degradation rates at 1000–1100 ℃. τ1-NiTaAl and β-NiAl phases exhibited different oxidation behaviors. NiAlTa alloys were more resistant to attack by mixed salts than pure salts. NiTaAl phase accelerated the alloy failure by acting as a fast diffusion channel for corrosive media. The oxidation mechanisms, hot corrosion mechanisms, and the effects of Ta were discussed.