High Strength and High Damping of AA6061/Zn Multilayer Composites Processed by Accumulative Roll Bonding
收藏中国科学院兰州化学物理研究所科学数据中心2025-12-12 更新2026-01-10 收录
下载链接：
https://ggjsfwdata.licp.cn/dataDetails/8a102a15f2ef456496be90e9bbc74223
下载链接
链接失效反馈官方服务：
资源简介：
AA6061 aluminum/zinc (AA6061/Zn) multilayer composites are fabricated by the accumulative roll bonding (ARB) technique. The microstructure, mechanical properties, and internal friction (IF) of the composites are characterized. The strength increases consistently with the number of rolling cycles, with the highest ultimate tensile strength of ≈300 MPa observed in the ARB6 sample subjected to
six cycles and the highest total elongation of ≈11% in the ARB3 sample subjected to three cycles. The amplitude-dependent IF measured at room temperature indicates that ARB can significantly improve the damping capacity of the composites, and the highest damping value (Q1) of 0.06 was obtained in ARB3 sample at a strain amplitude of 4 104. The high damping of the sample
is mainly ascribed to the stress-induced motion of high-density geometrically necessary dislocations in pure Zn layers. This study provides an effective and lowcost strategy of preparing Al strip with high damping capacity and superior mechanical properties.