Substructure development through dynamic recrystallisation in an austenitic Ni–30� alloy

This data looks at the effect of grain boundary movement on the characteristics of substructure development within the DRX regime. Different thermo-mechanical processing routes were employed to produce a range of DRX grain sizes at a given deformation temperature. The development of dislocation substructure was investigated using electron back-scattered diffraction (EBSD) in conjunction with transmission electron microscopy (TEM).