Raw data used to create depth of indentation versus time plots
用于绘制压痕深度与时间关系曲线图的原始数据
应用场景：
创建时间：
2018-03-30
相关数据集
Small punch tensile/fracture test data for P91 material at -100 °C and a displacement rate of .0055 mm/s (repeat test)
Data produced during work to evaluate the creep and fracture properties of P91 steel by small punch testing. The tests were performed on material extracted from the same pipe used in the INTEGRITY FP
DataCite Commons2020-10-05 更新70
Uniaxial creep test data for 2.25 Cr 1Mo V mod material at 550 °C and a stress of 190 MPa
Data collection created in the scope of a programme designed to evaluate the reliability of the Small Punch (SP) testing method as an alternative mechanical test technique for evaluation of the residu
DataCite Commons2020-10-05 更新50
Uniaxial creep test data for X10CrMoVNb9 1 - sj material at 580 °C and a stress of 140 MPa
Data generated in the scope of a project to investigate the influence of weld strength reduction on long-term integrity of power plant components made from heat-resistant martensitic steels.
DataCite Commons2020-10-10 更新30
Test data for uniaxial creep on material 1 CrMoV Rotor at 550 Celsius and a stress of 139 MPa (fifth repeat test)
Data consisting of results from 540 uniaxial creep tests and 43 cyclic creep tests performed on a range of engineering alloys at the National Physical Laboratory in the UK.
DataCite Commons2020-10-10 更新50
Test data for uniaxial creep on material ALLOY 800H at 850 Celsius and a stress of 15.33 MPa
The creep rupture data in this collection were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating
DataCite Commons2020-10-05 更新40