Calcium aluminate cement conversion analysed by ptychographic nanotomography

Raw data for:  Calcium aluminate cement conversion analysed by ptychographic nanotomography

doi: https://doi.org/10.1016/j.cemconres.2020.106201

Calcium aluminate cements are used for special applications but are nowadays banned for general structural purposes. This banning is due to the calcium aluminate hydrate conversion, that has led, for concretes fabricated with high water contents, to many building collapses. The stoichiometries of these conversion chemical reactions are relatively well established but the consequences in porosity, key to predict and ensure durability, were unknown. Here, we have used hard X-ray ptychographic nanotomography to study the hydration of CaAl2O4 at different temperatures and chiefly, at 4ºC and then at 50ºC to provoke conversion similar to field conditions. The mass densities of the resulting Al(OH)3 gels were 1.94, 1.98 and 2.23 g.cm-3, for samples hydrated at 4, 20 and 50ºC, respectively. These values are lower than that of gibbsite, 2.42 g.cm-3, the reference value used so far. Above all, this 3D imaging technique has allowed measuring the secondary water porosity developed in the conversion, which has an average pore dimension close to 140 nm. This work shows the way for porosity studies at the mesoscale in unaltered specimens.