EDX Analysis to quantify atoms deposition

The EDX test is important for calculating the elements deposited onto the surface. The results of EDX analysis are taken from different temperature parameters, then they will be compared between the use of low and high temperatures preheating. Also, samples using the preheating will be compared with samples that do not use the preheating. During the EDX measurement, different areas were focused and the corresponding peaks are shown in Figure 9. Figure 9. Energy Dispersive X-ray (EDX) analysis to quantify the deposition of atoms on the surface. (a) Sample S4, (b) Sample S1, (c) Sample S2, (d) Sample S3. (M: martensite, MC: metal carbide).能量色散X射线（Energy Dispersive X-ray, EDX）测试对于计算沉积于试样表面的元素含量至关重要。 本次EDX分析的测试结果取自不同温度参数条件下的试样，随后将对比采用低温预热与高温预热工艺的试样分析结果；同时，还将对比采用预热工艺与未采用预热工艺的试样分析结果。 在EDX测试过程中，研究人员选取了不同区域进行聚焦检测，对应的特征峰如图9所示。 图9 用于定量表征表面原子沉积情况的能量色散X射线（EDX）分析结果。(a) 试样S4，(b) 试样S1，(c) 试样S2，(d) 试样S3。(M：马氏体，MC：金属碳化物)