Supplement File

supplementary material for details on the change in observed MR ratio and 𝛥RA with Mn
387 content in CMFG for the as-deposited, 250{degree sign}C and 350{degree sign}C PA Type-I sample; in-plane R-H curves for
388 the 350 {degree sign}C PA Type-II sample at three different compositions viz. Co2FeGe, Co2Mn0.5Fe0.5Ge and
389 Co2Mn0.9Ge0.1; change in observed MR ratio and 𝛥RA with Mn content in CMFG for the 350{degree sign}C PA
390 Type-II sample; out-of-plane MR curves in the temperature range of 300 K to 50 K for the 350{degree sign}C
391 PA Type-II sample at three different compositions viz. Co2FeGe, Co2Mn0.5Fe0.5Ge and
392 Co2Mn0.9Fe0.1Ge; R-Ib curves at 50 K for several constant μ0Hz values for the 350{degree sign}C PA Type-II
393 sample at three different compositions viz. Co2FeGe, Co2Mn0.5Fe0.5Ge and Co2Mn0.9Fe0.1Ge; and the
394 table showing the summary of MR properties studied at room temperature for the CPP-GMR
395 devices containing Co2MnxFe1-xGe (0 {less than or equal to} x {less than or equal to} 1) Heusler as ferromagnetic layer electrode with
396 metallic spacers.

本材料详述了在CMFG中含Mn387的PA Type-I样品的沉积态下，于250°C和350°C条件下观察到的磁阻比（MR）以及ΔRA的变化；展示了350°C PA Type-II样品在不同组成（即Co2FeGe、Co2Mn0.5Fe0.5Ge和Co2Mn0.9Ge0.1）下的平面磁阻-磁场（R-H）曲线；描述了350°C PA Type-II样品中Mn含量对磁阻比及ΔRA的影响；提供了350°C PA Type-II样品在不同组成（即Co2FeGe、Co2Mn0.5Fe0.5Ge和Co2Mn0.9Fe0.1Ge）下的法向磁阻曲线；在50K温度下，针对350°C PA Type-II样品的几个固定μ0Hz值，给出了R-Ib曲线；并附有表格，总结了在室温条件下对含有Co2MnxFe1-xGe（0 ≤ x ≤ 1）Heusler作为铁磁层电极、金属间隔的CPP-GMR器件所研究的磁阻特性概要。