Apical adaptation, sealing ability and push-out bond strength of five root-end filling materials

This study compared the fluid filtration, adaptation to the root canal walls, and the push-out bond strength of two resin-based sealers and three calcium silicate-based retrograde filling materials. Fifty maxillary canines were shaped using manual instruments and the apical portion was sectioned. Retrograde cavities of 3-mm depth were prepared. The specimens were divided into five groups (n = 10): Sealer 26 (S26); MBPc (experimental); MTA; Portland cement with 20% zirconium oxide (PC/ZO), and Portland cement with 20% calcium tungstate (PC/CT). The fluid filtration was measured at 7 and 15 days. To evaluate the interfacial adaptation, sections of the teeth, 1 and 2 mm from the apex, were prepared and the percentage of gaps was calculated. The push-out bond strength at 2 mm from the apex was evaluated. Statistical analysis was performed using the ANOVA/Tukey’s test (p