Raw and processed data phase relationships in the SiO2-SrO-Al2O3 system

The liquidus lines in the silica rich area of the ternary SiO2-SrO-Al2O3 phase diagram were determined experimentally at 1723 K (1450°C), 1823 K (1550°C), and 1873K (1600°C) using the quenching technique. Quenched samples were analyzed using LOM, SEM and XRD. Based on the obtained results, the liquidus lines were constructed at these three temperatures. In this table the sample compositions studied, the equilibrating temperature and the phases present are listed.本研究采用淬火技术（quenching technique），在1723 K（1450℃）、1823 K（1550℃）及1873 K（1600℃）三个温度下，对SiO₂-SrO-Al₂O₃三元相图的富硅区域液相线（liquidus lines）开展了实验测定。通过光学显微镜（LOM）、扫描电子显微镜（SEM）与X射线衍射（XRD）对淬火试样进行分析后，基于所得实验结果绘制了上述三个温度下的液相线。本表格列出了所研究的试样成分、平衡温度以及存在的物相。