Data for: ELECTROCHEMICAL ALTERNATIVE TO OBTAIN REDUCED GRAPHENE OXIDE BY PULSE POTENTIAL: EFFECT OF SYNTHESIS PARAMETERS AND STUDY OF CORROSION PROPERTIES
收藏资源简介：
Figure 1. XRD patterns of selected ERGO powders obtained by one step route at -2 and -3 V VSCE and different thermal treatments (r.t., 200, 400, 600 and 800 °C). Figure 2. Raman spectroscopy of ERGO/304L SS samples showing fitting of D1 and D2 bands (-1, -2 and -4 VSCE), also it is show Raman spectra of samples where it was not possible to obtain and satisfactory analysis. Table 1. Data obtained from Raman fitting on coated 304L SS substrates where it is seen FWHM, Area, peak position, ID/IG and I2D/IG ratio
图1 一步法制备的、在相对于饱和甘汞电极（VSCE）电位-2 V与-3 V下合成且经不同热处理（室温、200、400、600和800 ℃）的ERGO粉末的X射线衍射（XRD）图谱。 图2 ERGO/304L不锈钢（SS）样品的拉曼光谱，展示了在-1、-2和-4 VSCE电位下制备的样品的D1与D2谱带拟合结果，同时还呈现了无法获得满意分析结果的样品的拉曼光谱。 表1 涂层304L不锈钢基体的拉曼峰拟合数据，其中包含半高宽（Full Width at Half Maximum）、峰面积、峰位、ID/IG与I2D/IG比值