A method of manufacturing a film having low oxygen transmission rate values

A method of manufacturing a film having an oxygen transmission rate (OTR) value in the range of 0.1 to 200 cc/m*24h at 23°C， 50 % relative humidity (RH)， and an OTR value in the range of 0.1 to 2000 cc/m*24h at 38°C at 85 % RH， comprising at least 60 % by weight nanocellulose based on the weight of the total amount of fibers in the film， wherein the method comprises the steps of， providing an aqueous suspension comprising said nanocellulose; forming a web from said aqueous suspension; calendering said web at a line load of at least 40 kN/m， and at a temperature of at least 60°C wherein said film is formed and said web has an OTR value in the range of 50 to 10000 cc/m*24h at 23°C， 50 % RH before said calendering step， or more preferably in the range of 500 to 5000 cc/m*24h at 23°C， 50 % RH before said calendering step.