Miniature Creep Rupture Testing of Steel comprising 2 1/4 Cr 1 Mo (Heat-Affected Zone Constituent)

Temperature iso-stress miniature creep tests were conducted on Heat-Affected Zone samples consisting of 2 1/4 Cr 1 Mo Steel under constant load and constant temperature in a vacuum environment on machines located at the Australian Nuclear Science and Technology Organisation. Test specimens conform to the nominal ratio of Lo=5D (6mm and 5mm Thread Diameter). Values for creep-extension, temperature and time were recorded at 30 minute intervals for the duration of the test.

本数据集针对2 1/4 Cr 1 Mo钢热影响区（Heat-Affected Zone）试样开展恒温恒应力微型蠕变试验：试验在澳大利亚核科学与技术组织（Australian Nuclear Science and Technology Organisation）的试验机上进行，试验环境为真空，全程保持恒定载荷与恒定温度。试验试样符合Lo=5D的名义比例，螺纹直径分别为6mm与5mm。试验全程以30分钟为间隔，记录蠕变伸长量、试验温度与试验时长数据。