Notch Effect in Carbon Fiber Reinforced Acrylonitrile Styrene Acrylate (ASA-CF): Tensile and Fracture Tests - FRADDCO project

This dataset contains tensile and fracture tests of specimens made of carbon fiber reinforced acrylonitrile–styrene–acrylate (ASA-CF) material, manufactured by fused filament fabrication (FFF). The files include 9 tensile specimens and 72 single-edge-notch bending (SENB) specimens containing U-notches with different nominal notch radii (from 0 mm -crack-like defects- up to 2.0 mm) and fabricated with three different raster orientations: 0/90, 30/−60 and 45/−45.本数据集包含采用熔融沉积成型（fused filament fabrication，FFF）制备的碳纤维增强丙烯腈-苯乙烯-丙烯酸酯（carbon fiber reinforced acrylonitrile–styrene–acrylate，ASA-CF）材料试样的拉伸与断裂试验数据。数据集文件涵盖9个拉伸试样，以及72个带有不同名义缺口半径（范围为0mm——类裂纹缺陷——至2.0mm）U型缺口的单边缺口弯曲（single-edge-notch bending，SENB）试样；上述单边缺口弯曲试样均采用三种不同的填充取向制备：0/90、30/−60以及45/−45。