Non-local modelling of twinning in polycrystalline AZ31

Figure data used for the paper "A non-local model for the description of twinning in polycrystalline materials in the context of infinitesimal strains: application to a magnesium alloy" (10.46298/jtcam.7562). Specifically, the following data is included : Figure 3a : fig_behavior_compression_modified_model.txt (X, Y for solid curve) + fig_behavior_compression_modified_exp.txt (X, Y for experimental points)<br> Figure 3b : fig_activity_compression_modified.txt (X, Y Bas, Y Pri, Y Pyr et Y TTw for solid curves). Dots: first point of the curve.<br> Figure 5a : fig_schmid_onset.txt (X Local, X Global, Y)<br> Figure 5b : fig_schmid_end.txt (X Local, X Global, Y)<br> Figure 6 : fig_path_equivalentstress.txt (X, Y Equivalent stress) + fig_path_twinvolumefraction.txt (X, Y Twin volume fraction)<br> Figure 7a : fig_post3_sig.txt (X, Y, size)<br> Figure 7b : fig_post10_sig.txt (X, Y, size)<br> Figure 8a : fig_post3_tau.txt (X, Y, size)<br> Figure 8b : fig_post10_tau.txt (X, Y, size)<br> Figure 9a : fig_behavior_compressiontension_model.txt (X, Y for solid curve) + fig_behavior_compressiontension_exp.txt (X, Y for experimental points)<br> Figure 9b : fig_activity_compressiontension_modified.txt (X, Y Bas, Y Pri, Y Pyr et Y TTw for solid curves). Dots: first point of the curve.<br> Figure 10a : fig_basal0_modified_parent.txt (X, Y, size for parent grains)<br> Figure 10b : fig_basal5_modified_parent.txt (X, Y, size for parent grains) + fig_basal5_modified_child.txt (X, Y, size size for child grains)<br> Figure 10c : fig_basal13_modified_parent.txt (X, Y, size for parent grains) et fig_basal13_modified_child.txt (X, Y, size for child grains)<br> Figure 11a : fig_behavior_convergence_64.txt (X, Y for curve 64^3) + fig_behavior_convergence_96.txt (X, Y for curve 96^3) + fig_behavior_convergence_128.txt (X, Y for curve 128^3) + fig_behavior_convergence_192.txt (X, Y for curve 192^3)<br> Figure 11b : fig_local_convergence_128.txt (X, Y, size for points 128^3) + fig_local_convergence_192.txt (X, Y, size for points 192^3)本数据集为论文《无穷小应变框架下多晶材料孪晶描述的非局部模型（non-local model）：在镁合金中的应用》（DOI:10.46298/jtcam.7562）的配套配图数据。具体包含以下数据：<br>图3a：对应文件fig_behavior_compression_modified_model.txt（实线曲线的X、Y数据）与fig_behavior_compression_modified_exp.txt（实验测点的X、Y数据）<br>图3b：对应文件fig_activity_compression_modified.txt，其实线曲线包含Y_Bas、Y_Pri、Y_Pyr及Y_TTw数据（横轴为X），散点为曲线的首个测点<br>图5a：对应文件fig_schmid_onset.txt，包含施密特（Schmid）起始相关的局部X、全局X及Y数据<br>图5b：对应文件fig_schmid_end.txt，包含施密特（Schmid）终止相关的局部X、全局X及Y数据<br>图6：对应文件fig_path_equivalentstress.txt（等效应力（equivalent stress）的X、Y数据）与fig_path_twinvolumefraction.txt（孪晶体积分数（twin volume fraction）的X、Y数据）<br>图7a：对应文件fig_post3_sig.txt，包含X、Y及数据点尺寸数据<br>图7b：对应文件fig_post10_sig.txt，包含X、Y及数据点尺寸数据<br>图8a：对应文件fig_post3_tau.txt，包含X、Y及数据点尺寸数据<br>图8b：对应文件fig_post10_tau.txt，包含X、Y及数据点尺寸数据<br>图9a：对应文件fig_behavior_compressiontension_model.txt（实线曲线的X、Y数据）与fig_behavior_compressiontension_exp.txt（实验测点的X、Y数据）<br>图9b：对应文件fig_activity_compressiontension_modified.txt，其实线曲线包含Y_Bas、Y_Pri、Y_Pyr及Y_TTw数据（横轴为X），散点为曲线的首个测点<br>图10a：对应文件fig_basal0_modified_parent.txt，包含基面（basal）母晶粒（parent grains）的X、Y及数据点尺寸数据<br>图10b：对应文件fig_basal5_modified_parent.txt（基面母晶粒的X、Y及数据点尺寸数据）与fig_basal5_modified_child.txt（基面子晶粒（child grains）的X、Y及数据点尺寸数据）<br>图10c：对应文件fig_basal13_modified_parent.txt（基面母晶粒的X、Y及数据点尺寸数据）与fig_basal13_modified_child.txt（基面子晶粒的X、Y及数据点尺寸数据）<br>图11a：包含fig_behavior_convergence_64.txt（64³网格收敛特性曲线的X、Y数据）、fig_behavior_convergence_96.txt（96³网格收敛特性曲线的X、Y数据）、fig_behavior_convergence_128.txt（128³网格收敛特性曲线的X、Y数据）及fig_behavior_convergence_192.txt（192³网格收敛特性曲线的X、Y数据）<br>图11b：对应文件fig_local_convergence_128.txt（128³网格散点的X、Y及数据点尺寸数据）与fig_local_convergence_192.txt（192³网格散点的X、Y及数据点尺寸数据）